'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PC/PET X7200MR-NA9A002 SABIC INNOVATIVE US
142
Form：Granules | Grade：Injection grade
Properties:
Flame retardantHigh heat resistance
Typical Applications:
Automotive ApplicationsElectronic and electrical accessories
Product Description
Certificates(0)
Datasheet
Product Description
| Typical Applications: | Automotive Applications | Electronic and electrical accessories |
| Properties: | Flame retardant | High heat resistance |
Certificates
No Data...
Technical Data Sheet
| optical performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Refractive index | ISO 489 | 1.557 | ||
| transmissivity | 2540μm | ASTM D1003 | 88.0 | % |
| turbidity | 2540μm | ASTM D1003 | 1.1 | % |
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
| Impact strength of cantilever beam gap | -10°C | ISO 180/1A | 5.0 | kJ/m² |
| 23°C | ISO 180/1A | 8.0 | kJ/m² | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 95.0 | J |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| UL flame retardant rating | 3.0mm | UL 94 | V-2 | |
| Burning wire flammability index | 1.0mm | IEC 60695-2-12 | 750 | °C |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| bending strength | Yield,50.0mmSpan | ASTM D790 | 84.0 | Mpa |
| ISO 178 | 75.0 | Mpa | ||
| Bending modulus | ISO 178 | 2000 | Mpa | |
| 50.0mmSpan | ASTM D790 | 1960 | Mpa | |
| Tensile strain | Break | ISO 527-2/50 | >150 | % |
| elongation | Break | ASTM D638 | 140 | % |
| Tensile strain | Yield | ISO 527-2/5 | 5.0 | % |
| elongation | Yield | ASTM D638 | 5.0 | % |
| tensile strength | Break | ISO 527-2/50 | 56.0 | Mpa |
| Break | ASTM D638 | 56.0 | Mpa | |
| Yield | ISO 527-2/50 | 55.0 | Mpa | |
| Tensile modulus | ASTM D638 | 1880 | Mpa | |
| ISO 527-2/1 | 2000 | Mpa | ||
| tensile strength | Yield | ASTM D638 | 55.0 | Mpa |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| thermal conductivity | ISO 8302 | 0.23 | W/m/K | |
| Linear coefficient of thermal expansion | TD：23to60°C | ISO 11359-2 | 8E-05 | cm/cm/°C |
| TD：-40to40°C | ASTME831 | 1.1E-04 | cm/cm/°C | |
| MD：23to60°C | ISO 11359-2 | 8E-05 | cm/cm/°C | |
| MD：-40to40°C | ASTME831 | 1.1E-04 | cm/cm/°C | |
| Ball Pressure Test | 105°C | IEC 60695-10-2 | Pass | |
| Vicat softening temperature | ISO 306/B120 | 115 | °C | |
| ASTM D15259 | 115 | °C | ||
| Hot deformation temperature | 1.8MPa,Unannealed,100mmSpan | ISO 75-2/Ae | 99.0 | °C |
| 1.8MPa,Unannealed,3.20mm | ASTM D648 | 90.0 | °C | |
| 0.45MPa,Unannealed,3.20mm | ASTM D648 | 96.0 | °C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| melt mass-flow rate | 265°C/2.16kg | ASTM D1238 | 12 | g/10min |
| Melt Volume Flow Rate (MVR) | 265°C/2.16kg | ISO 1133 | 12.0 | cm3/10min |
| Shrinkage rate | MD：3.20mm | Internal Method | 0.50-0.70 | % |
| TD：3.20mm | Internal Method | 0.50-0.70 | % | |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Volume resistivity | ASTM D257 | >1.0E+15 | ohms·cm | |
| Surface resistivity | ASTM D257 | >1.0E+15 | ohms | |
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Shore hardness | ShoreD,10Sec | ASTM D2240 | 76 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.