Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.05 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO2039-1 | 80.0 MPa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Dimensional ChangeafterHeating | | DIN15105-1/-2 | 5.0 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 1730 MPa |
| Tensile stress | | ISO527-2 | 18.0 MPa |
| Tensile stress | | ISO527-2 | 24.0 MPa |
| Tensile strain | | ISO527-2 | 2.9 % |
| Flexural modulus | | ISO178 | 1850 MPa |
| Bending stress | | ISO178 | 34.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1fA | 6.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1fA | 9.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | IEC243 | 160 kV/mm |
| dielectric constant | | IEC60250 | 2.50 |
| dielectric constant | | IEC60250 | 2.50 |
| Dissipation Factor | | IEC60250 | >1.0E-4 |
| Dissipation Factor | | IEC60250 | >1.0E-4 |
| Surface Resistivity | | IEC60093 | >1.0E+13 ohms |
| Volume resistivity | | IEC60093 | >1.0E+16 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ISO306/B50 | 92.0 °C |
| | DIN53752 | 8E-05 cm/cm/°C |
| thermal conductivity | | ISO11501 | 0.16 W/m/K |
| | ISO75-2 | 82 °C |
| Maximum operating temperature - continuous use | | DIN52612 | 70 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare