PA66 Vydyne® R228

Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
density		ISO 1183	1.48 g/cm³
Shrinkage rate		ISO 294-4	1.0 %
Shrinkage rate	Shrinkage rate		ISO 294-4	1.1 %
Water absorption rate		ISO 62	1.1 %
Water absorption rate	Water absorption rate		ISO 62	1.6 %

Supplementary Information	Test Condition	Test Method	Test Result
Automotive Materials		FMVSS302	+

Mechanical properties	Test Method	Test Result
Poisson's ratio	ISO 527	0.40
Tensile strain	ISO 527-2	6.0 %
Flexural modulus	ISO 178	6100 MPa
bending strength	ISO 178	124 MPa
Tensile modulus	ISO 527-2	6900 MPa
tensile strength	ISO 527-2	103 MPa
Tensile strain	ISO 527-2	1.5 %

Impact resistance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength		ISO 179/1eA	6.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ISO 179/1eA	7.0 kJ/m²
Impact strength of simply supported beam without notch		ISO 179/1eU	110 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch		ISO 179/1eU	140 kJ/m²
Impact strength of cantilever beam gap		ISO 180	7.0 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ISO 180	9.0 kJ/m²

Thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature (HDT)		ISO 75-2/B	222 °C
Hot deformation temperature (HDT)	Hot deformation temperature (HDT)		ISO 75-2/A	118 °C
melting temperature		ISO 11357-3	258 °C
		ISO 11359-2	6.3E-04 cm/cm/°C
			ISO 11359-2	6E-04 cm/cm/°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.