Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Thermosetting components | | | 16 hr |
| Thermosetting components | Resin | | 100 |
| Thermosetting components | Hardener | | 按重量计算的混合比:90 |
| Thermosetting components | Pot Life | | 2.5 min |
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| Curing Time | | | 1.0 hr |
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.20 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 72 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| AbrasionIndex-NBS | | | 425 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ASTM D790 | 586 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 640 J/m |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D412 | 25.9 MPa |
| tensile strength | | ASTM D412 | 60.7 MPa |
| elongation | Break | ASTM D412 | 260 % |
| tear strength | Split | ASTM D470 | 20 kN/m |
| compression set | | ASTM D395A | 10 % |
| Shore hardness | | ASTM D2632 | 58 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| brittle temperature | | ASTM D746 | <-70.0 °C |
| Heat distortion temperature | | | 145 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare