'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PA612 153HSL-NC010 DUPONT USA
243
Form：Granules | Grade：Injection grade
Properties:
Mineral reinforcementThermal stability
Typical Applications:
Engineering accessoriesAutomotive Applications
Product Description
Certificates(1)
Datasheet
Product Description
| Typical Applications: | Engineering accessories | Automotive Applications |
| Properties: | Mineral reinforcement | Thermal stability |
Certificates
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak | |
| -30°C | ISO 179/1eU | NoBreak | ||
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| Burning rate | 1.00mm | ISO 3795 | <100 | mm/min |
| UL flame retardant rating | 0.9mm | UL 94 | HB | |
| 1.5mm | UL 94 | HB | ||
| 0.9mm | IEC 60695-11-10,-20 | HB | ||
| 1.5mm | IEC 60695-11-10,-20 | HB | ||
| Extreme Oxygen Index | ISO 4589-2 | 27 | % | |
| FMVSS flammability | FMVSS302 | B | ||
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Tensile strain | Yield | ISO 527-2 | 4.4 | % |
| tensile strength | Yield | ISO 527-2 | 62.0 | Mpa |
| Tensile modulus | ISO 527-2 | 2400 | Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | 30 | % | |
| Bending modulus | ISO 178 | 2100 | Mpa | |
| Wear resistance | ISO 4649 | 6.00 | mm³ | |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Linear coefficient of thermal expansion | MD：-- | ISO 11359-2 | 1.2E-04 | cm/cm/°C |
| Melting temperature | ISO 11357-3 | 218 | °C | |
| Vicat softening temperature | ISO 306/B50 | 180 | °C | |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO 75-2/A | 62.0 | °C |
| 0.45MPa,Unannealed | ISO 75-2/B | 135 | °C | |
| Linear coefficient of thermal expansion | TD：EffectiveThermalDiffusivity | ISO 11359-2 | 7E-08 | m²/s |
| TD：55to160°C | ISO 11359-2 | 1.8E-04 | cm/cm/°C | |
| TD：-40to23°C | ISO 11359-2 | 9E-05 | cm/cm/°C | |
| TD：-- | ISO 11359-2 | 1.2E-04 | cm/cm/°C | |
| MD：55to160°C | ISO 11359-2 | 1.7E-04 | cm/cm/°C | |
| MD：-40to23°C | ISO 11359-2 | 9E-05 | cm/cm/°C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Stickiness | 96%H2SO4 | ISO 307 | 115 | cm³/g |
| Water absorption rate | Equilibrium,23°C,2.00mm,50%RH | ISO 62 | 1.3 | % |
| Shrinkage rate | TD | ISO 294-4 | 1.4 | % |
| Water absorption rate | Saturation,23°C,2.00mm | ISO 62 | 3.0 | % |
| Shrinkage rate | MD | ISO 294-4 | 1.3 | % |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Relative permittivity | 100Hz | IEC 60250 | 3.60 | |
| Dielectric strength | IEC 60243-1 | 30 | KV/mm | |
| Volume resistivity | IEC 60093 | 1E+15 | ohms·cm | |
| Surface resistivity | IEC 60093 | -- | ohms | |
| Relative permittivity | 1MHz | IEC 60250 | 3.20 | |
| Dissipation factor | 100Hz | IEC 60250 | 0.014 | |
| 1MHz | IEC 60250 | 0.016 | ||
| Compared to the anti leakage trace index | IEC 60112 | PLC 0 | ||
| film | Test Condition | Test Method | Test Result | Test Unit |
| Tensile strain | Yield，MD | ISO 527-3 | 4.4 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.