Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| refractive index | | ASTM D-542 | 1.49 |
| Full light transmission system | | ASTM D-1003 | 93 % |
| processability | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTM D-955 | 0.2-0.5 % |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ASTM D-570 | 0.3 % |
| melt mass-flow rate | | ASTM D-1238 | 6.0 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D-638 | 69[700] MPa[KG/cm |
| Izod impact strength | | ASTM D-256 | 16[1.6] J/m[kg.cm/cm] |
| bending strength | | ASTM D-790 | 103[1050] MPa[KG/cm |
| | ASTM D-790 | 3.0[3.1×10 GPa[KG/cm |
| Rockwell hardness | | ASTM D-785 | 92 M Scale |
| Extension rate | | ASTM D-638 | 7 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| volume resistivity | | JIS K-6911 | ＞10 m[cm] |
| Surface Resistivity | | JIS K-6911 | ＞10 |
| arc resistance | | JIS K-6911 | 没有痕迹 |
| Insulation breakdown strength | | | 20[20] MV/m[KV/mm] |
| dielectric loss tangent | | | 0.05 |
| dielectric constant | | | 3.7 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| specific heat | | JIS K-7123 | 1.5[0.35] J/g.c[(cal/g/℃)] |
| Load deflection temperature | | ASTM D-648 | 89 °C |
| | ASTM D-177 | 0.2 W/m℃ |
| spiral flow | | MRC | 190-290 mm |
| linear expansion coefficient | | ASTM D-696 | 6×10 1/℃ |
| vicat | | ASTM D-1525 | 104 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.