Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.29 g/cm³ |
| melt mass-flow rate | | ISO1133 | 50到60 g/10min |
| Shrinkage rate | | ISO294-4,ISO2577 | 1.0 % |
| Shrinkage rate | | ISO294-4,ISO2577 | 0.90 % |
| Water absorption rate | | ISO62 | 0.35 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | | ISO527-2 | 70.0 MPa |
| Tensile strain | Yield | ISO527-2 | 7.8 % |
| Flexural modulus | | ISO178 | 2400 MPa |
| Bending stress | | ISO178 | 105 MPa |
| Tensile modulus | | ISO527-2 | 2270 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO180/A | 68 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC60093 | >1.0E+15 ohms·cm |
| Surface Resistivity | | IEC60093 | >1.0E+15 ohms |
| dielectric strength | | IEC60243-1 | 44 kV/mm |
| dielectric constant | | IEC60250 | 3.80 |
| dielectric constant | | IEC60250 | 3.70 |
| Dissipation Factor | | IEC60250 | 1.5E-03 |
| Dissipation Factor | | IEC60250 | 8.6E-03 |
| CTI | | IEC60112 | 150 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO75-2/A | 196 °C |
| Glass Transition Temperature | | ISO11357-2,DSC | 220 °C |
| | ISO11359-2 | 5.5E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.