PP Copolymer

PP Copolymer WINTEC™ WFX4TA Japan Polychem Corporation

Compare

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
gloss		ASTM D523	90
turbidity	1000μm	ISO 14782	15 %

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	0°C	ISO 179	2.0 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179	8.0 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2	800 MPa
tensile strength	Yield	ISO 527-2	22.0 MPa
Nominal tensile fracture strain		ISO 527-2	>400 %
Bending modulus		ISO 178	750 MPa
bending strength		ISO 178	25.0 MPa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	70.0 °C
Vicat softening temperature		ISO 306	110 °C
Crystallization peak temperature		ISO 11357-3	125 °C

Physical properties	Test Condition	Test Method	Test Result
density		ISO 1183	0.900 g/cm³
melt mass-flow rate		ISO 1133	7.0 g/10min

hardness	Test Condition	Test Method	Test Result
Rockwell hardness		ISO 2039-2	75

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.