Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTMD1238 | 15 g/10min |
| Melt volume flow rate | | ISO1133 | 15.0 cm³/10min |
| Shrinkage rate | | 内部方法 | 0.50到0.80 % |
| Shrinkage rate | | 内部方法 | 0.40到0.60 % |
| Water absorption rate | | ISO62 | 0.49 % |
| Water absorption rate | | ISO62 | 0.15 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ASTMD2240 | 74 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| transmissivity | | ASTMD1003 | 88.0 % |
| Haze ratio | | ASTMD1003 | <2.0 % |
| refractive index | | ISO489 | 1.539 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Burning wire flammability index | | IEC60695-2-12 | 750 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Dart impact equipped with measuring instruments | | ASTMD3763 | 95.0 J |
| Charpy Notched Impact Strength | | ISO179/1eA | 70 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| fracture | | ASTMD638 | 46.0 MPa |
| fracture | | ISO527-2/50 | 54.0 MPa |
| yield | | ASTMD638 | 47.0 MPa |
| yield | | ISO527-2/50 | 55.0 MPa |
| yield | | ASTMD638 | 5.0 % |
| yield | | ISO527-2/50 | 5.0 % |
| fracture | | ASTMD638 | 150 % |
| fracture | | ISO527-2/50 | >200 % |
| yield | | ASTMD790 | 71.0 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ASTMD257 | >1.0E+15 ohms |
| Volume resistivity | | ASTMD257 | >1.0E+15 ohms·cm |
| Compared to the Leakage Tracking Index (CTI) | | UL746 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| BallPressure Test | | IEC60695-10-2 | Pass |
| Flow:- | | ASTME831,ISO11359-2 | 1.1E-04 cm/cm/°C |
| Flow: | | ISO11359-2 | 9E-05 cm/cm/°C |
| Horizontally:- | | ASTME831,ISO11359-2 | 1.1E-04 cm/cm/°C |
| Horizontally: | | ISO11359-2 | 9E-05 cm/cm/°C |
| thermal conductivity | | ISO8302 | 0.23 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.