Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO 1133 | 0.45 g/10min |
| Environmental stress cracking resistance | | ASTM D1693 | >600 hr |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ISO 868 | 58 |
| other | Test Condition | Test Method | Test Result |
|---|
| characteristic | | | 冲击强度 |
| purpose | | | 洗涤剂容器、洗发水容器、化妆品容器 |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO 1133 | 0.45 g/10min |
| density | | ISO 1183 | 935 kg/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | | ISO 527-2 | >500 % |
| Flexural modulus | | ISO 178 | 550 Mpa |
| Tensile modulus | | ISO 527-2 | 550 Mpa |
| tensile strength | | ISO 527-2 | 17.0 Mpa |
| Tensile stress | | ISO 527-2 | 17 Mpa |
| elongation | | ISO 527-2 | ＞500 % |
| Tensile modulus | | ISO 527-1 | 550 Mpa |
| Flexural modulus | | ISO 178 | 550 Mpa |
| Dart impact | | ISO 179-1 | NB KJ/m |
| Shore hardness | | ISO 868 | 58 |
| Environmental stress cracking resistance | | ASTM D-1693 | ＞600 hours |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179 | 无断裂 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792/ISO 1183 | 0.935 |
| melt mass-flow rate | | ASTM D1238/ISO 1133 | 0.45 g/10min |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ISO 306 | 119 °C |
| melting temperature | | ISO 11357-3 | 126 °C |
| vicat | | ISO 306 | 119 °C |
| melting temperature | | ISO 11357-3 | 126 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare