PPA/F/PTFE LNP™ LUBRICOMP™ UFL-4036HS BK8115
30
- Properties:Thermal stabilityFlame retardant
- Usages:tubingLighting applications
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ASTMD955 | 0.20to0.40 % | |
| ASTMD955 | 0.80to1.0 % | ||
| Water absorption rate | ASTMD570 | 0.15 % | |
| ISO62 | 0.25 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile stress | ISO527-2/5 | 192 Mpa | |
| Tensile strength 4 | ASTMD638 | 189 Mpa | |
| Tensile stress | ISO527-2/5 | 192 Mpa | |
| elongation | ASTMD638 | 1.8 % | |
| Tensile strain | ISO527-2/5 | 2.0 % | |
| elongation | ASTMD638 | 1.7 % | |
| Tensile strain | ISO527-2/5 | 2.0 % | |
| Flexural modulus | ASTMD790 | 10600 Mpa | |
| Bending modulus 6 | ISO178 | 11300 Mpa | |
| Flexural Strength5 | ASTMD790 | 242 Mpa | |
| Tensile modulus | ASTMD638 | 15400 Mpa | |
| ASTMD638 | 15400 Mpa | ||
| ISO527-2/1 | 12600 Mpa | ||
| Tensile strength 4 | ASTMD638 | 189 Mpa | |
| Flexural Strength5 | ASTMD790 | 233 Mpa | |
| ASTMD3702Modified | 0.48 | ||
| ASTMD3702Modified | 0.52 | ||
| Wear factor | ASTMD3702Modified | 0.100 10^-10in^5-min/ft-lb-hr | |
| ASTMD3702Modified | 5.00 10^-10in^5-min/ft-lb-hr |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Multi axis Instrumented Impact Energy | ISO6603-2 | 2.00 J | |
| NotchedIzodImpactStrength7 | ISO180/1A | 9.1 kJ/m² | |
| UnnotchedIzodImpactStrength7 | ISO180/1U | 47 kJ/m² | |
| Dart impact equipped with measuring instruments | ASTMD3763 | 8.90 J |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ASTMD648 | 277 °C | ||
| ISO75-2/Af | 273 °C | ||
| ASTMD696 | 2.1E-05 cm/cm/°C | ||
| ASTMD696 | 4.5E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.