POM 500AL DUPONT USA

Form：Granules | Grade：Injection grade

Properties:

Dimensional stabilityFatigue resistanceHigh impact resistance

Typical Applications:

Household appliancesBottle capIndustrial applicationsAutomotive sectorElectronic fieldElectrical field

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Household appliances \| Bottle cap \| Industrial applications \| Automotive sector \| Electronic field \| Electrical field
Properties:	Dimensional stability \| Fatigue resistance \| High impact resistance

Certificates

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23°C	ISO 179/1eA	7.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	6.0	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	130	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	160	kJ/m²
Impact strength of cantilever beam gap	-40°C	ISO 180/1A	5.0	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	6.0	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Burning rate	1.00mm	ISO 3795	28	mm/min
UL flame retardant rating	0.8mm	IEC 60695-11-10,-20	HB
	UL flame retardant rating	1.5mm	UL 94	HB
	UL flame retardant rating	UL flame retardant rating	0.8mm	UL 94	HB
FMVSS flammability		FMVSS302	B
UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Bending modulus		ISO 178	2800	Mpa
Tensile modulus		ISO 527-2	3000	Mpa
Tensile creep modulus	1000hr	ISO 899-1	1600	Mpa
Tensile creep modulus	Tensile creep modulus	1hr	ISO 899-1	2400	Mpa
Nominal tensile fracture strain		ISO 527-2	23	%
Tensile strain	Yield	ISO 527-2	11	%
tensile strength	Yield	ISO 527-2	66.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
AnnealingTime-Optional			30.0	min/mm
AnnealingTemperature			160	°C
Linear coefficient of thermal expansion	TD	ISO 11359-2	1.2E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ISO 11359-2	1.2E-04	cm/cm/°C
Melting temperature		ISO 11357-3	178	°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	97.0	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	164	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	0.30	%
Shrinkage rate	MD	ISO 294-4	1.8	%
Shrinkage rate	Shrinkage rate	TD	ISO 294-4	1.7	%
Melt Volume Flow Rate (MVR)	190°C/2.16kg	ISO 1133	12.0	cm3/10min
melt mass-flow rate		ISO 1133	14	g/10min
density		ISO 1183	1.39	g/cm³
MediumDensity			1.18	g/cm³
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
Emission		VDA275	<8.00	mg/kg

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.