ABS/PMMA BF-0370 K21294 Samsung Cheil South Korea

Form：Granules

Properties:

High temperature resistanAging resistanceHigh impact resistance

Typical Applications:

Automotive componentsCastersElectronic and electrical componentsElectrical appliances

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive components \| Casters \| Electronic and electrical components \| Electrical appliances
Properties:	High temperature resistan \| Aging resistance \| High impact resistance

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23°C	ISO 180/1A	11	kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	16	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.0mm	UL 94	HB
	UL flame retardant rating	1.5mm	UL 94	HB
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ISO 178	90.0	Mpa
bending strength	bending strength		ASTM D790	74.0	Mpa
tensile strength	Yield	ISO 527-2/50	45.0	Mpa
tensile strength	tensile strength	Yield	ASTM D638	44.0	Mpa
Tensile modulus		ISO 527-2/50	2400	Mpa
Bending modulus		ISO 178	2700	Mpa
Bending modulus	Bending modulus		ASTM D790	2500	Mpa
Tensile strain	Break	ISO 527-2/50	10	%
elongation	Break	ASTM D638	25	%
tensile strength	Break	ISO 527-2/50	48.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature	--	ISO 306/B120	104	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	102	°C
Hot deformation temperature	1.8MPa,Annealed,4.00mm	ISO 75-2/A	101	°C
	Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ISO 75-2/A	84.0	°C
		Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	89.0	°C
			Hot deformation temperature	0.45MPa,Annealed,4.00mm	ISO 75-2/B	104	°C
			Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,4.00mm	ISO 75-2/B	96.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	MD：3.20mm	ASTM D955	0.30-0.60	%
melt mass-flow rate	220°C/10.0kg	ISO 1133	15	g/10min
melt mass-flow rate	melt mass-flow rate	220°C/10.0kg	ASTM D1238	15	g/10min
hardness	Test Condition	Test Method	Test Result	Test Unit
Pencil hardness		JISK5401	HB
Rockwell hardness	R-Scale	ISO 2039-2	115
Rockwell hardness	Rockwell hardness	R-Scale	ASTM D785	113

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.