PA6 BKV35H2.0 ENVALIOR WUXI

Form：Granules | Grade：Injection grade

Properties:

35% glass fiber reinforceEasy to flowThermal stability rating

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Properties:

35% glass fiber reinforce | Easy to flow | Thermal stability rating

Certificates

No Data...

Technical Data Sheet

Other performance	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	260℃；2.16kg	ISO 1133	43	cm3/10min
Fiberglass content		ISO 3451-1	35	%
density		ISO 1183	1.396	g/cm³
machinability	Test Condition	Test Method	Test Result	Test Unit
Injection speed		ISO 294	200	mm/s
Mold temperature		ISO 294	80	°C
Melt Temperature		ISO 294	260	°C
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Bending modulus	2mm/min	ISO 178	9500(5900)	Mpa
Elongation at Break	5mm/min	ISO 527-1	3.0	%
Tensile stress	2mm/min，0.035	ISO 178	270(150)	Mpa
Tensile modulus	1mm/min	ISO 527-1	10500(6700)	Mpa
bending strength	2mm/min	ISO 178	4.0(6.0)	%
bending strength	bending strength	2mm/min	ISO 178	280(180)	Mpa
tensile strength	5mm/min	ISO 527-1	190(115)	Mpa
Impact strength of cantilever beam gap	23℃	ISO 180-1U	75	kJ/m²
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.80MPa	ISO 75-1	210	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.