Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTMD1238 | 0.90 g/10min |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| gloss | | ASTMD2457 | 56 |
| Haze ratio | | ASTMD1003 | 14 % |
| gloss | | ASTM D-2457 | 56 |
| Haze ratio | | ASTM D-1003 | 14 % |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| film thickness | | | 50.8 um |
| density | | ASTM D-792 | 0.921 g/m3 |
| melt mass-flow rate | | ASTM D-1238 | 0.9 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tangent modulus (MD) | | ASTM D-882 | 168 Mpa |
| Tangent modulus (TD) | | ASTM D-882 | 238 Mpa |
| Tensile yield strength (TD) | | ASTM D-882 | 14.6 Mpa |
| Tensile yield strength (MD) | | ASTM D-882 | 14.2 Mpa |
| Tensile fracture strength (TD) | | ASTM D-882 | 39.2 Mpa |
| Tensile strength at break (MD) | | ASTM D-882 | 48.8 Mpa |
| Falling hammer impact | | ASTM D-1709A | 300 g |
| Elmendorf Tear Strength (MD) | | ASTM D-1922 | 720 g |
| Elmendorf Tear Strength (TD) | | ASTM D-1922 | 1000 g |
| Other performance | Test Condition | Test Method | Test Result |
|---|
| Movie Piercing Resistance | | Internal Method | 6.62 J/cm³ |
| film | Test Condition | Test Method | Test Result |
|---|
| Elmondov tear strength | | ASTMD1922 | 1000 g |
| Secant modulus | | ASTMD882 | 168 Mpa |
| Secant modulus | | ASTMD882 | 238 Mpa |
| tensile strength | | ASTMD882 | 14.2 Mpa |
| tensile strength | | ASTMD882 | 14.6 Mpa |
| tensile strength | | ASTMD882 | 48.8 Mpa |
| tensile strength | | ASTMD882 | 39.2 Mpa |
| elongation | | ASTMD882 | 660 % |
| elongation | | ASTMD882 | 740 % |
| Falling hammer impact | | ASTMD1709A | 300 g |
| Elmondov tear strength | | ASTMD1922 | 720 g |
| Film thickness - tested | | | 51 µm |
| Film Puncture Force | | 内部方法 | 6.62 J/cm³ |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ASTMD1525 | 107 °C |
| Melting temperature (DSC) | | 内部方法 | 120 °C |
| vicat | | ASTM D-1525 | 107 °C |
| melting temperature | | Internal Method | 120 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.