PA66 A50H1 BK SOLVAY SHANGHAI

196

Form：Granules | Grade：Flame retardant grade

Supplier(5)

Product Description

Certificates(0)

Datasheet

Product Description

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	80 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	90	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.40 mm	UL 94	V-0
	UL flame retardant rating	0.8 mm	UL 94	V-0
		UL flame retardant rating	1.6 mm	UL 94	V-0
		UL flame retardant rating	UL flame retardant rating	3.2 mm	UL 94	V-0
Burning wire flammability index	0.8 mm	IEC 60695-2-12	960	°C
	Burning wire flammability index	1.6 mm	IEC 60695-2-12	960	°C
	Burning wire flammability index	Burning wire flammability index	3.2 mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	0.40 mm	IEC 60695-2-13	960	°C
	Hot filament ignition temperature	0.8 mm	IEC 60695-2-13	960	°C
	Hot filament ignition temperature	Hot filament ignition temperature	1.6 mm	IEC 60695-2-13	775	°C
Extreme Oxygen Index		ISO 4589-2	33	%
European Railways Certifications	R22	EN 45545-2	HL3
European Railways Certifications	European Railways Certifications	R23	EN 45545-2	HL3
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	23°C	ISO 178	135	Mpa
bending strength	bending strength	23°C	ASTM D790	125	Mpa
Bending modulus	23°C	ISO 178	3700	Mpa
Bending modulus	Bending modulus	23°C	ASTM D790	3800	Mpa
Tensile strain	Break, 23°C	ISO 527-2	12	%
tensile strength	Break, 23°C	ISO 527-2/1A	80.0	Mpa
tensile strength	tensile strength	Yield, 23°C	ISO 527-2/1A	85.0	Mpa
Tensile modulus	23°C	ISO 527-2/1A	3800	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			80	°C
Suggested maximum moisture content			0.20	%
Temperature at the rear of the barrel			260 to 270	°C
Temperature in the middle of the barrel			265 to 275	°C
Temperature at the front of the material cylinder			265 to 275	°C
Mold temperature			60 to 80	°C
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/Af	85.0	°C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/Bf	237	°C
Melting temperature		ISO 11357-3	263	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Outdoor applicability		UL 746C	f1
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	2.7	%
Water absorption rate	Water absorption rate	24 hr, 23°C	ISO 62	0.88	%
Shrinkage rate	Flow	ISO 294-4	1.5	%
Shrinkage rate	Shrinkage rate	横向Flow	ISO 294-4	1.3	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index	Solution A	IEC 60112	PLC 0
Dissipation factor		IEC 60250	0.017
Relative permittivity		IEC 60250	3.50
Dielectric strength	2.00 mm	IEC 60243-1	21	KV/mm
Dielectric strength	Dielectric strength	0.800 mm	IEC 60243-1	33	KV/mm
Volume resistivity		IEC 60093	3.0E+15	ohms·cm
Surface resistivity		IEC 60093	3.0E+15	ohms

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PA66 A50H1 BK SOLVAY SHANGHAI

Product Description

Certificates

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index