Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| shelf-life | | | 52 wk |
| shelf-life | | | 1.0 wk |
| shelf-life | | | 0.29 wk |
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | | 2.04 g/cm³ |
| Apparent density | | | 1.00 g/cm³ |
| spiral flow length | | | 71.0 cm |
| Shrinkage rate | | | 0.50 % |
| Water absorption rate | | | 0.026 % |
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| Curing Time | | | 8.3E-03 hr |
| Curing Time | | | 0.017to0.050 hr |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | | 97 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Loss factor | | | 0.0320 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | | 86.2 MPa |
| Flexural modulus | | | 17200 MPa |
| bending strength | | | 124 MPa |
| compressive strength | | | 276 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | | 21 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | | >1.0E+16 ohms |
| Volume resistivity | | | >5.0E+16 ohms·cm |
| dielectric strength | | | >16 kV/mm |
| dielectric constant | | | 4.50 |
| Dissipation Factor | | | 7E-03 |
| arc resistance | | | 180 sec |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | | 8.7E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | | 1.3 W/m/K |
| Linear coefficient of thermal expansion | | | 200 °C |
| Heat distortion temperature | | | 110 °C |
| Glass Transition Temperature | | | 130 °C |
| Linear coefficient of thermal expansion | | | 3.2E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.