Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.30 g/cm³ |
| Water absorption rate | | ASTMD570 | 0.25 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Limiting Oxygen Index | | ASTMD2863 | 22 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | Break | ASTM D790 | 75.0 MPa |
| tensile strength | Break | ASTMD638 | 56.0 MPa |
| elongation | Break | ASTMD638 | >10 % |
| Flexural modulus | | ASTMD790 | 2200 MPa |
| bending strength | | ISO 178 | 75.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179 | 5.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ASTM D256 | NoBreak |
| Charpy Notched Impact Strength | | ASTM D256 | 5.00 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179 | 无断裂 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTMD257 | 1E+16 ohms·cm |
| dielectric strength | | ASTMD149 | 50 kV/mm |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Compared to the Leakage Tracking Index (CTI) | | ASTM D3638 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | ASTMD2117 | 225 °C |
| Heat distortion temperature | | ASTMD648 | 165 °C |
| Heat distortion temperature | | ASTMD648 | 60.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.