Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.20 g/cm³ |
| density | | ISO 1183/B | 1.20 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 22 g/10min |
| melt mass-flow rate | | ISO 1133 | 22 g/10min |
| Water absorption rate | | ASTM D570 | 0.15 % |
| Water absorption rate | | ISO 62 | 0.15 % |
| Water absorption rate | | ASTM D570 | 0.32 % |
| Water absorption rate | | ISO 62 | 0.32 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 118 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | ASTM D542 | 1.586 |
| refractive index | | ISO 489 | 1.586 |
| transmissivity | | ASTM D1003 | 89.0 % |
| Haze ratio | | ASTM D1003 | 1.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Average degree of combustion | | ASTM D635 | 3 cm |
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | V-2 |
| UL flame retardant rating | | UL 94 | V-2 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Taber abraser | | ASTM D1044 | 45 % |
| elongation | Break | ASTM D638 | 120 % |
| Tensile modulus | | ISO 527-2/50 | 2340 MPa |
| tensile strength | Yield | ASTM D638 | 60.0 MPa |
| tensile strength | Yield | ISO 527-2/50 | 60.0 MPa |
| tensile strength | Break | ASTM D638 | 65.5 MPa |
| tensile strength | Break | ISO 527-2/50 | 66.0 MPa |
| Tensile modulus | | ASTM D638 | 2340 MPa |
| Tensile strain | Break | ISO 527-2/50 | 120 % |
| Flexural modulus | | ASTM D790 | 2410 MPa |
| Flexural modulus | | ISO 178 | 2410 MPa |
| bending strength | | ASTM D790 | 96.5 MPa |
| bending strength | | ISO 178 | 96.5 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 750 J/m |
| Impact strength of cantilever beam gap | | ISO 180/A | 73 kJ/m² |
| InstrumentedDartImpact | | ASTM D3763 | 72.3 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | 2E+17 ohms·cm |
| dielectric strength | | ASTM D149 | 17 kV/mm |
| dielectric strength | | IEC 60243-1 | 17 kV/mm |
| dielectric constant | | ASTM D150 | 3.00 |
| dielectric constant | | ASTM D150 | 3.00 |
| Dissipation Factor | | ASTM D150 | 1E-03 |
| Dissipation Factor | | ASTM D150 | 2E-03 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | ASTM D696 | 6.8E-05 cm/cm/°C |
| Heat distortion temperature | | ASTM D648 | 142 °C |
| Heat distortion temperature | | ISO 75-2/B | 142 °C |
| Heat distortion temperature | | ASTM D648 | 126 °C |
| Heat distortion temperature | | ISO 75-2/A | 126 °C |
| Heat distortion temperature | | ASTM D648 | 126 °C |
| Heat distortion temperature | | ISO 75-2/A | 126 °C |
| vicat | | ASTM D15257 | 152 °C |
| vicat | | ISO 306/B50 | 152 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.