PC IR2200 CB FIPC TAIWAN

169

Form：Granules | Grade：Injection grade

Properties:

Low viscosityHigh mobility

Typical Applications:

Thin walled products

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Thin walled products
Properties:	Low viscosity \| High mobility

Certificates

No Data...

Technical Data Sheet

machinability	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate		ASTM D-955	0.5-0.7	%
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	300℃ 1.2kg	ISO 1133 (ASTM D-1238)	12	g/10min
density		ASTM D-792	1.2
Water absorption rate	23℃水中24h	ASTM D-570	0.23	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	4mm with notch 3.2mm with notch	ISO 180 (ASTM D-256)	70	KJ/m
Bending modulus		ISO 178 (ASTM D-790)	2350	Mpa
Taber abraser	1,000round	ASTM D-1044	12	mg
tensile strength	Yield	ISO R-527 (ASTM D-638)	64	Mpa
bending strength		ISO 178 (ASTM D-790)	93	Mpa
Tensile modulus		ISO R-527 (ASTM D-638)	2300	Mpa
Rockwell hardness		ISO 2039-2 (ASTM D-785)	120	R
tensile strength	Break	ISO R-527 (ASTM D-638)	68	Mpa
Elongation at Break		ISO R-527 (ASTM D-638)	115	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature		ISO 306	148	°C
Combustibility	1.47mm厚	UL -94	V-2
Linear coefficient of thermal expansion		ASTM D-696 (ASTM D-695)	6.5	×10
Hot deformation temperature	1.8Mpa 18.6kg/cm	ISO 75 (ASTM D-648)	132	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Total Light Transmittance	3mm厚	ASTM D-1003	85-89	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.