PC L-1225L TEIJIN JAPAN

Form：Granules | Grade：Injection grade

Properties:

High mobilityFlame retardant

Typical Applications:

Electrical appliancesElectrical fieldElectronic field

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electrical appliances \| Electrical field \| Electronic field
Properties:	High mobility \| Flame retardant

Certificates

No Data...

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
Refractive index		ASTM D542	1.585
transmissivity	3000μm	ASTM D1003	88.0	%
Transmittance rate		ASTM D1003/ISO 13468	88	%
Refractive index		ASTM D542/ISO 489	1.585
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch		ISO 179	NoBreak
flammability	Test Condition	Test Method	Test Result	Test Unit
Burning wire flammability index	3.0mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	1.5mm	IEC 60695-2-13	875	°C
Hot filament ignition temperature	Hot filament ignition temperature	3.0mm	IEC 60695-2-13	850	°C
UL flame retardant rating	1.9mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	0.40mm	UL 94	V-2
Burning wire flammability index	1.5mm	IEC 60695-2-12	850	°C
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2/1	2400	Mpa
tensile strength	Yield	ISO 527-2/50	61.0	Mpa
Tensile strain	Yield	ISO 527-2/50	6.0	%
Nominal tensile fracture strain		ISO 527-2/50	>50	%
Bending modulus		ISO 178	2350	Mpa
bending strength		ISO 178	93.0	Mpa
Tensile modulus		ASTM D638/ISO 527	2400	kg/cm²(MPa)[Lb/in²]
elongation		ASTM D638/ISO 527	6	%
Bending modulus		ASTM D790/ISO 178	2350	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	93	kg/cm²(MPa)[Lb/in²]
Elongation at Break		ASTM D638/ISO 527	>50	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	139	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	126	°C
Vicat softening temperature		ISO 306/B50	146	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	7E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	7E-05	cm/cm/°C
RTI Elec	1.5mm	UL 746	125	°C
RTI Imp	1.5mm	UL 746	115	°C
RTI Str	1.5mm	UL 746	125	°C
Vicat softening temperature		ASTM D1525/ISO R306	146	℃（℉）
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	0.7	mm/mm.℃
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	18.0	cm3/10min
Shrinkage rate	TD:4.00mm	Internal Method	0.50-0.70	%
Shrinkage rate	Shrinkage rate	MD:4.00mm	Internal Method	0.50-0.70	%
Water absorption rate	23°C,24hr	ISO 62	0.20	%
Shrinkage rate		ASTM D955	0.5-0.7	%
Water absorption rate		ASTM D570/ISO 62	0.2	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	>1.0E+15	ohms
Volume resistivity		IEC 60093	>1.0E+15	ohms·cm
Dielectric strength		IEC 60243-1	30	KV/mm
Relative permittivity	100Hz	IEC 60250	3.10
Relative permittivity	Relative permittivity	1MHz	IEC 60250	3.00
Dissipation factor	100Hz	IEC 60250	1E-03
Dissipation factor	Dissipation factor	1MHz	IEC 60250	9E-03
Compared to the anti leakage trace index		IEC 60112	PLC 2
Surface resistivity		ASTM D257/IEC 60093	>1×1015	Ω
Dielectric constant		ASTM D150/IEC 60250	3
Dielectric constant	Dielectric constant		ASTM D150/IEC 60250	3.1
Arc resistance		ASTM D495/IEC 60112	30
Volume resistivity		ASTM D257/IEC 60093	>1×1013	Ω.cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.