PA66 27GFT HENAN SHENMA HUAWEI

Form：Granules

Properties:

Flame retardantGlass fiber reinforcedHigh temperature resistanGlass fiber content 28.4%

Typical Applications:

Automotive External PartsElectrical applications

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive External Parts \| Electrical applications
Properties:	Flame retardant \| Glass fiber reinforced \| High temperature resistan \| Glass fiber content 28.4%

Certificates

No Data...

Technical Data Sheet

Other performance	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	平行，-	-	--	%
Shrinkage rate	Shrinkage rate	垂直，-	-	--	%
UL flame retardant rating		UL 94	--
density		ISO 1183	--	g/cm³
Water absorption rate	23℃Saturation	ISO 62	--	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	Dry	ISO 527	--	GPa
Impact strength of cantilever beam gap	Dry	ISO 180	--	kJ/m²
bending strength	Dry	ISO 178	226.6	Mpa
tensile strength	Dry	ISO 527	151.4	Mpa
Elongation at Break	Dry	ISO 527	5.3	%
Bending modulus	Dry	ISO 178	10	GPa
Impact strength of simply supported beam without notch	Dry	ISO 179	52.4	kJ/m²
Charpy Notched Impact Strength	Dry	ISO 179	19.0	kJ/m²
thermal performance	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	Dry	ISO 1133	--	g/10min
Linear coefficient of thermal expansion		ISO 11359	--	10-5k
Hot deformation temperature	1.80MPa	ISO 75	--	°C
Melting temperature	Dry	ISO 3146	--	°C
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity	Dry/湿态	IEC 93	--	Ω.cm
Dielectric strength	Dry	IEC 243	--	KV/mm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.