| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.45to1.49 g/cm³ |
| density | | ASTM D792 | 1.45to1.49 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| DurometerHardness | | ASTM D2240 | 76to82 |
| DurometerHardness | | ASTM D2240 | 76to82 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | ASTM D635 | HB |
| UL flame retardant rating | | ASTM D635 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 80 J/m |
| Impact strength of cantilever beam gap | | ASTM D256 | 170 J/m |
| Dart impact | | ASTM D4226 | 66.7 J/cm |
| Dart impact | | ASTM D4226 | 267 J/cm |
| Impact strength of cantilever beam gap | | ASTM D256 | 80 J/m |
| Impact strength of cantilever beam gap | | ASTM D256 | 170 J/m |
| Dart impact | | ASTM D4226 | 66.7 J/cm |
| Dart impact | | ASTM D4226 | 267 J/cm |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 2620 MPa |
| tensile strength | | ASTM D638 | 42.1 MPa |
| Flexural modulus | | ASTM D790 | 2650 MPa |
| bending strength | | ASTM D790 | 80.0 MPa |
| Tensile modulus | | ASTM D638 | 2620 MPa |
| tensile strength | | ASTM D638 | 42.1 MPa |
| Flexural modulus | | ASTM D790 | 2650 MPa |
| bending strength | | ASTM D790 | 80.0 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 72.2 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 6.5E-05 cm/cm/°C |
| Heat distortion temperature | | ASTM D648 | 72.2 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 6.5E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.