optical performance	Test Condition	Test Method	Test Result	Test Unit
gloss	60°, 无织构	ASTM D523	95
impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C, Total Energy	ASTM D3763	25.0	J
Dart impact	Dart impact		N	107	J/cm
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5 mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ASTM D638	1790	Mpa
tensile strength	Yield	ASTM D638	41.0	Mpa
tensile strength	tensile strength	Break	ASTM D638	34.0	Mpa
elongation	Break	ASTM D638	40	%
Bending modulus	50.0 mm Span	ASTM D790	1790	Mpa
bending strength	Yield, 50.0 mm Span	ASTM D790	58.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	87.0	°C
	Hot deformation temperature	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	90.0	°C
		Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	76.0	°C
			Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	79.0	°C
			Hot deformation temperature	Hot deformation temperature	1.8 MPa, Annealed	ASTM D648	95.0	°C
Vicat softening temperature		ASTM D15256	99.0	°C
Linear coefficient of thermal expansion	Flow : -30 to 0°C	ASTM E831	8.5E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	8.6E-5	cm/cm/°C
		Linear coefficient of thermal expansion	Flow : 0 to 100°C	ASTM E831	9.0E-5	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	9.2E-5	cm/cm/°C
RTI Elec		UL 746	50.0	°C
RTI Imp		UL 746	50.0	°C
RTI		UL 746	50.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	220°C/10.0 kg	ASTM D1238	7.0	g/10 min
melt mass-flow rate	melt mass-flow rate	260°C/5.0 kg	ASTM D1238	13	g/10 min
Shrinkage rate	3.20 mm，Flow	Internal Method	0.50 - 0.70	%
Water absorption rate	Equilibrium, 23°C	ASTM D570	0.55	%
Outdoor applicability		UL 746C	f2
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		ASTM D257	> 1.0E+15	ohms
Dielectric strength	3.20 mm, in Oil	ASTM D149	16	KV/mm
Dielectric constant	60 Hz	ASTM D150	5.20
	Dielectric constant	50 kHz	ASTM D150	5.20
	Dielectric constant	Dielectric constant	1 MHz	ASTM D150	3.21
Dissipation factor	50 Hz	ASTM D150	0.15
	Dissipation factor	60 Hz	ASTM D150	0.15
	Dissipation factor	Dissipation factor	1 MHz	ASTM D150	0.026
Compared to the anti leakage trace index		UL 746	PLC 0
High arc combustion index		UL 746	PLC 0
Hot wire ignition		UL 746	PLC 3
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	86

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.