| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.07 g/cm³ |
| Apparent density | | | 0.59 g/cm³ |
| Melt volume flow rate | | ISO1133 | 5.50 cm³/10min |
| Shrinkage rate | | ISO294-4 | 0.50to0.90 % |
| Water absorption rate | | ISO62 | 1.7 % |
| Water absorption rate | | ISO62 | 0.35 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO2039-1 | 65.0 MPa |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | | ISO527-2 | 3.5 % |
| Tensile creep modulus | | ISO899-1 | 1100 MPa |
| Bending stress | | ISO178 | 60.0 MPa |
| Tensile modulus | | ISO527-2 | 2000 MPa |
| Tensile stress | | ISO527-2 | 42.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179 | 9.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO179 | 40 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/A | 10 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/A | 30 kJ/m² |
| film | Test Condition | Test Method | Test Result |
|---|
| elongation | Break | ISO527-3 | 11 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric constant | | IEC60250 | 3.80 |
| Dissipation Factor | | IEC60250 | 9E-03 |
| Dissipation Factor | | IEC60250 | 0.026 |
| Surface Resistivity | | IEC60093 | 1E+13 ohms |
| Volume resistivity | | IEC60093 | 1E+14 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 100 °C |
| | ISO75-2/A | 95.0 °C |
| vicat | | ISO306/A50 | 104 °C |
| vicat | | ISO306/B50 | 90.0 °C |
| | ISO11359-2 | 8.0E-5to1.1E-4 cm/cm/°C |
| thermal conductivity | | DIN52612 | 0.17 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.