'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PC 3412ECR GY8D279 SABIC INNOVATIVE NANSHA
62
Form：Granules | Grade：Injection grade
Properties:
Glass fiber reinforcedenhanceFlame retardantHigh rigidity
Typical Applications:
Plastic bagAutomotive External PartsIndustrial applicationsElectrical appliancesLighting applicationsMedical supplies
Product Description
Certificates(1)
Datasheet
Product Description
| Typical Applications: | Plastic bag | Automotive External Parts | Industrial applications | Electrical appliances | Lighting applications | Medical supplies |
| Properties: | Glass fiber reinforced | enhance | Flame retardant | High rigidity |
Certificates
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 35 | kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 20.0 | J |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 40 | kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ASTM D256 | 110 | J/m |
| 23°C | ASTM D256 | 110 | J/m | |
| -30°C | ISO 180/1A | 6.0 | kJ/m² | |
| 23°C | ISO 180/1A | 7.0 | kJ/m² | |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 35 | kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 5.0 | kJ/m² |
| 23°C | ISO 179/1eA | 6.0 | kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 40 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| UL flame retardant rating | 1.5mm | UL 94 | V-0 | |
| 3.0mm | UL 94 | 5VA | ||
| Burning wire flammability index | 1.0mm | IEC 60695-2-12 | 960 | °C |
| Hot filament ignition temperature | 1.0mm | IEC 60695-2-13 | 825 | °C |
| Extreme Oxygen Index | ISO 4589-2 | 40 | % | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| tensile strength | Break | ISO 527-2/5 | 90.0 | Mpa |
| Break | ASTM D638 | 87.0 | Mpa | |
| Yield | ISO 527-2/5 | 95.0 | Mpa | |
| Yield | ASTM D638 | 90.0 | Mpa | |
| Tensile modulus | ISO 527-2/1 | 6000 | Mpa | |
| ASTM D638 | 5500 | Mpa | ||
| elongation | Yield | ASTM D638 | 3.1 | % |
| Tensile strain | Yield | ISO 527-2/5 | 2.8 | % |
| Break | ISO 527-2/5 | 3.2 | % | |
| Bending modulus | 50.0mmSpan | ASTM D790 | 5000 | Mpa |
| ISO 178 | 5500 | Mpa | ||
| bending strength | ISO 178 | 140 | Mpa | |
| Yield,50.0mmSpan | ASTM D790 | 156 | Mpa | |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| RTI Imp | UL 746 | 130 | °C | |
| RTI Elec | UL 746 | 130 | °C | |
| Linear coefficient of thermal expansion | TD：23to80°C | ISO 11359-2 | 7E-05 | cm/cm/°C |
| TD：-40to40°C | ASTME831 | 7E-05 | cm/cm/°C | |
| MD：23to80°C | ISO 11359-2 | 3E-05 | cm/cm/°C | |
| MD：-40to40°C | ASTME831 | 3E-05 | cm/cm/°C | |
| Ball Pressure Test | 125°C | IEC 60695-10-2 | Pass | |
| Vicat softening temperature | -- | ISO 306/B120 | 146 | °C |
| -- | ISO 306/B50 | 145 | °C | |
| ASTM D152510 | 147 | °C | ||
| Hot deformation temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO 75-2/Af | 136 | °C |
| RTI Str | UL 746 | 130 | °C | |
| Hot deformation temperature | 0.45MPa,Unannealed,64.0mmSpan | ISO 75-2/Bf | 141 | °C |
| 1.8MPa,Unannealed,3.20mm | ASTM D648 | 141 | °C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Water absorption rate | Equilibrium,23°C,50%RH | ISO 62 | 0.12 | % |
| Saturation,23°C | ISO 62 | 0.29 | % | |
| Shrinkage rate | TD：3.20mm | Internal Method | 0.20-0.50 | % |
| MD：3.20mm | Internal Method | 0.20-0.50 | % | |
| Melt Volume Flow Rate (MVR) | 300°C/1.2kg | ISO 1133 | 7.00 | cm3/10min |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 7.0 | g/10min |
| density | ISO 1183 | 1.36 | g/cm³ | |
| ASTM D792 | 1.30 | g/cm³ | ||
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Surface resistivity | IEC 60093 | >1.0E+15 | ohms | |
| Volume resistivity | IEC 60093 | >1.0E+15 | ohms·cm | |
| Relative permittivity | 50Hz | IEC 60250 | 3.30 | |
| 60Hz | IEC 60250 | 3.30 | ||
| 1MHz | IEC 60250 | 3.30 | ||
| Dissipation factor | 50Hz | IEC 60250 | 0.020 | |
| 60Hz | IEC 60250 | 0.020 | ||
| 1MHz | IEC 60250 | 0.010 | ||
| Arc resistance | ASTM D495 | PLC7 | ||
| Compared to the anti leakage trace index | CTI | UL 746 | PLC 3 | |
| High arc combustion index | HAI | UL 746 | PLC 3 | |
| High voltage arc tracing rate | HVTR | UL 746 | PLC 3 | |
| Hot wire ignition | HWI | UL 746 | PLC 0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.