COC APEL™ APL5014CL MITSUI CHEM JAPAN
557
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 260°C/2.16kg | ASTMD1238 | 36 | g/10min |
| Shrinkage rate | MD | 内部方法 | 0.60 | % |
| TD | 内部方法 | 0.50 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tensile strength | 屈服 | ASTMD638 | 60.0 | Mpa |
| elongation | 断裂 | ASTMD638 | 3.0 | % |
| Bending modulus | ASTMD790 | 3200 | Mpa | |
| bending strength | ASTMD790 | 100 | Mpa | |
| Cantilever beam without notch impact strength | ASTMD256 | 10.0 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,未退火 | ASTMD648 | 125 | °C |
| Glass transition temperature | 内部方法 | 135 | °C | |
| Linear coefficient of thermal expansion | MD | ASTMD696 | 7E-05 | cm/cm/°C |
| TD | ASTMD696 | 6E-05 | cm/cm/°C |
| film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water vapor permeability | ASTMF1249 | 0.090 | g·mm/m²/atm/24hr |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Refractive index | ASTMD542 | 1.540 | ||
| Light transmittance | ASTMD1003 | 90.0 | % | |
| Haze | ASTMD1003 | <0.50 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.