Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTMD955 | 0.40到0.80 % |
| density | | ASTMD792 | 1.04 g/cm³ |
| melt mass-flow rate | | ASTMD1238 | 13 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTMD785 | 107 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | Injection | ASTMD638 | 3170 MPa |
| Flexural modulus | Injection | ASTMD790 | 3310 MPa |
| bending strength | Injection | ASTMD790 | 55.0 MPa |
| tensile strength | | ASTMD638 | 45.0 MPa |
| tensile strength | Injection | ASTMD638 | 45.0 MPa |
| elongation | | ASTMD638 | 3.0 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 21 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD648 | 87.0 °C |
| | ASTMD648 | 81.0 °C |
| vicat | | ASTMD1525 | 98.0 °C |
| | ASTMD696 | 9E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.