Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.29 g/cm³ |
| Apparent density | | ISO60 | 0.82 g/cm³ |
| Melt volume flow rate | | ISO1133 | 4.00 cm³/10min |
| Water absorption rate | | ISO62 | 0.60 % |
| Water absorption rate | | ISO62 | 0.15 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO868 | 71 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | IEC60695-11-10,-20 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 6.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 15 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 1000 MPa |
| Tensile stress | Break | ISO527-2 | 38.0 MPa |
| Tensile stress | | ISO527-2 | 31.0 MPa |
| Tensile stress | | ISO527-2 | 34.5 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| | IEC60250 | 3.70 |
| | IEC60250 | 3.40 |
| Dissipation Factor | | IEC60250 | 0.040 |
| CTI | | IEC60112 | 600 V |
| Volume resistivity | | IEC60093 | 1E+15 ohms·cm |
| dielectric strength | | IEC60243-1 | 23 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ISO306/B50 | 160 °C |
| melting temperature | | ISO11357-3 | 221 °C |
| | ISO11359-2 | 1.7E-04 cm/cm/°C |
| | ISO11359-2 | 1.7E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.