PLA TRANSMARE® BIO 35MI-10-0.001
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO1183 | 1.25 g/cm³ | |
| melt mass-flow rate | ISO1133 | 30 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO868 | 73 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| bending strength | ISO178 | 60.0 MPa | |
| Tensile stress | ISO527-2/50 | 20.0 MPa | |
| TensileStrain | ISO527-2/50 | 2.4 % | |
| Tensile strain | ISO527-2/50 | 6.0 % | |
| Flexural modulus | ISO178 | 2380 MPa | |
| Tensile modulus | ISO527-2/1 | 2370 MPa | |
| tensile strength | ISO527-2/50 | 42.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO179/1A | 1.5 kJ/m² | |
| ISO179/1A | 3.5 kJ/m² | ||
| ISO179/1A | 4.2 kJ/m² | ||
| ISO179/1A | 5.3 kJ/m² | ||
| Impact strength of simply supported beam without notch | ISO179/1U | 54 kJ/m² | |
| ISO179/1U | NoBreak | ||
| Impact strength of cantilever beam gap | ISO180/1A | 5.9 kJ/m² | |
| UnnotchedIzodImpactStrength | ISO180/1U | NoBreak |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO75-2/B | 51.0 °C | |
| ISO75-2/A | 49.0 °C | ||
| vicat | ISO306/A | 59.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.