PC/ABS D2000 BK SABIC INNOVATIVE JAPAN

Form：Granules | Grade：Injection grade

Properties:

wear resistant

Typical Applications:

Electrical appliancesPlastic bagAerospace Applications

Supplier(0)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electrical appliances \| Plastic bag \| Aerospace Applications
Properties:	wear resistant

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C, Energy at Peak	ASTM D3763	40.0	J
Dart impact	Dart impact	--	ISO 6603-2	45.0	J
Suspended wall beam without notch impact strength	23°C4	ISO 180/1U	140	kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ASTM D4812	无断裂
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Wear factor		ASTM D3702	1.2E+7	10^-8 mm³/N·m
Friction coefficient	Static	ASTM D3702	0.090
Friction coefficient	Friction coefficient	Dynamic	ASTM D3702	0.16
bending strength	--	ISO 178	78.0	Mpa
bending strength	bending strength	--	ASTM D790	82.0	Mpa
Bending modulus		ASTM D790	2130	Mpa
elongation	Break	ISO 527-2	99	%
	elongation	Break	ASTM D638	130	%
		elongation	Yield	ISO 527-2	5.6	%
		elongation	elongation	Yield	ASTM D638	6.5	%
tensile strength	Break	ISO 527-2	54.0	Mpa
	tensile strength	Break	ASTM D638	60.0	Mpa
		tensile strength	Yield	ISO 527-2	51.0	Mpa
		tensile strength	tensile strength	Yield	ASTM D638	53.0	Mpa
Tensile modulus	--	ISO 527-2/1	2120	Mpa
Tensile modulus	Tensile modulus	--2	ASTM D638	1860	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			100	°C
drying time			4.0	hr
Suggested maximum moisture content			0.020	%
Temperature at the rear of the barrel			295 to 305	°C
Temperature in the middle of the barrel			300 to 310	°C
Temperature at the front of the material cylinder			305 to 315	°C
Processing (melt) temperature			305 to 315	°C
Mold temperature			65 to 95	°C
Back pressure			0.200 to 0.300	Mpa
Screw speed			30 to 60	rpm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	142	°C
	Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span4	ISO 75-2/Bf	140	°C
		Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	130	°C
		Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span4	ISO 75-2/Af	128	°C
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	7.4E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	7.4E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	7.4E-5	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.18	%
Water absorption rate	Water absorption rate	24 hr, 50% RH	ASTM D570	0.14	%
Shrinkage rate	Flow : 24hr	ISO 294-4	0.70 - 0.90	%
	Shrinkage rate	横向Flow : 24hr	ISO 294-4	0.70 - 0.90	%
		Shrinkage rate	Across FlowFlow : 24hr	ASTM D955	0.70 - 0.90	%
		Shrinkage rate	Shrinkage rate	Flow : 24hr	ASTM D955	0.70 - 0.90	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.