PC D20001 BK1E055 SABIC INNOVATIVE US

Form：Granules | Grade：Injection grade

Properties:

wear resistant

Typical Applications:

Electrical appliancesPlastic bagAerospace Applications

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electrical appliances \| Plastic bag \| Aerospace Applications
Properties:	wear resistant

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Suspended wall beam without notch impact strength	23°C	ASTM D4812	1600	J/m
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C4	ISO 180/1U	100	kJ/m²
Dart impact	23°C, Energy at Peak	ASTM D3763	51.0	J
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5 mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	--2	ASTM D638	2550	Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2600	Mpa
tensile strength	Yield	ASTM D638	67.0	Mpa
	tensile strength	Yield	ISO 527-2	62.0	Mpa
		tensile strength	Break	ASTM D638	60.0	Mpa
		tensile strength	tensile strength	Break	ISO 527-2	54.0	Mpa
elongation	Yield	ASTM D638	4.5	%
	elongation	Yield	ISO 527-2	4.3	%
		elongation	Break	ASTM D638	6.5	%
		elongation	elongation	Break	ISO 527-2	6.7	%
Bending modulus	--	ASTM D790	2820	Mpa
Bending modulus	Bending modulus	--	ISO 178	2800	Mpa
bending strength	--	ASTM D790	103	Mpa
bending strength	bending strength	--	ISO 178	102	Mpa
Friction coefficient	Dynamic	ASTM D3702	0.090
Friction coefficient	Friction coefficient	Static	ASTM D3702	0.22
Wear factor		ASTM D3702	6.0E+6	10^-8 mm³/N·m
injection	Test Condition	Test Method	Test Result	Test Unit
Temperature in the middle of the barrel			255 to 265	°C
Temperature at the front of the material cylinder			260 to 270	°C
Processing (melt) temperature			255 to 290	°C
Mold temperature			40 to 65	°C
Back pressure			0.200 to 0.300	Mpa
Screw speed			30 to 60	rpm
Temperature at the rear of the barrel			250 to 260	°C
Suggested maximum moisture content			0.020	%
drying time			4.0 to 6.0	hr
drying temperature			80	°C
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	97.0	°C
	Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	89.0	°C
	Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span4	ISO 75-2/Af	94.0	°C
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	6.6E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	6.7E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	6.7E-5	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Melt Volume Flow Rate (MVR)	300°C/1.2 kg	ASTM D1238	15.7	cm3/10min
Shrinkage rate	Flow : 24hr	ASTM D955	0.50	%
	Shrinkage rate	Across FlowFlow : 24hr	ASTM D955	0.60	%
		Shrinkage rate	横向Flow : 24hr	ISO 294-4	0.57	%
		Shrinkage rate	Shrinkage rate	Flow : 24hr	ISO 294-4	0.53	%
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.12	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PC D20001 BK1E055 SABIC INNOVATIVE US

Product Description

Certificates

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index