PCTG AN004 EASTMAN USA

Form：Granules | Grade：Injection grade

Properties:

Easy to processheat-resisting

Typical Applications:

Household daily necessitiesElectrical applications

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Household daily necessities \| Electrical applications
Properties:	Easy to process \| heat-resisting

Certificates

SGS

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
turbidity		ASTM D1003	0.30	%
transmissivity	Regular	ASTM D1003	89.0	%
transmissivity	transmissivity	Total	ASTM D1003	91.0	%
impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C,EnergyatPeakLoad	ASTM D3763	42.0	J
Dart impact	Dart impact	-40°C,EnergyatPeakLoad	ASTM D3763	48.0	J
Impact strength of cantilever beam gap	23°C	ASTM D4218	NoBreak
	Impact strength of cantilever beam gap	-40°C	ASTM D4218	NoBreak
		Impact strength of cantilever beam gap	23°C	ISO 180	7.8	kJ/m²
			Impact strength of cantilever beam gap	-40°C	ISO 180	4.8	kJ/m²
				Impact strength of cantilever beam gap	23°C	ASTM D256	80	J/m
				Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-40°C	ASTM D256	40	J/m
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	Break,23°C	ASTM D638	51.0	Mpa
tensile strength	tensile strength	Break,23°C	ISO 527-2	46.0	Mpa
elongation	Yield,23°C	ASTM D638	5.0	%
tensile strength	Yield,23°C	ISO 527-2	47.0	Mpa
tensile strength	tensile strength	Yield,23°C	ASTM D638	47.0	Mpa
Tensile modulus	23°C	ISO 527-2	1800	Mpa
bending strength	Yield,23°C	ASTM D790	69.0	Mpa
bending strength	bending strength	23°C	ISO 178	65.0	Mpa
Bending modulus	23°C	ISO 178	1850	Mpa
Bending modulus	Bending modulus	23°C	ASTM D790	2000	Mpa
Tensile strain	Break,23°C	ISO 527-2	200	%
Tensile strain	Tensile strain	Yield,23°C	ISO 527-2	4.0	%
elongation	Break,23°C	ASTM D638	320	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	65.0	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	73.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	MD：3.20mm	ASTM D955	0.20-0.60	%
density		ASTM D792	1.20	g/cm³
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Sale,23°C	ASTM D785	103

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.