PC LC1700 IDEMITSU JAPAN

Form：Granules | Grade：Injection grade

Properties:

UV resistanceHigh mobilityAging resistanceoptical performance

Typical Applications:

LCDapplication

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	LCD \| application
Properties:	UV resistance \| High mobility \| Aging resistance \| optical performance

Certificates

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
characteristic			高流动.导光性
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	Yield	ISO 527-2	65	Mpa
Elongation at Break		ISO 527-2	95	%
Bending modulus		ISO 178	2300	Mpa
bending strength		ISO 178	90	Mpa
Charpy Notched Impact Strength		ISO 179	40	kJ/m²
Impact strength of cantilever beam gap		ASTM D256/ISO 179	40	kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	tB 80	%
tensile strength		ASTM D638/ISO 527	Y 65	kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	2.3(GPa)	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	90	kg/cm²(MPa)[Lb/in²]
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	128	°C
UL flame retardant rating	0.400 mm	UL 94	V-2
Combustibility (rate)		UL 94	V-2/0.4mm
Hot deformation temperature	HDT	ASTM D648/ISO 75	129	℃（℉）
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Melt Volume Flow Rate (MVR)	MVR	ISO 1133	40	cm3/10min
Shrinkage rate	TD	Internal Method	0.5-0.7	%
Shrinkage rate	Shrinkage rate	MD: 2.00 mm	Internal Method	0.5-0.7	%
Water absorption rate	Equilibrium,23℃, 50% RH	ISO 62	0.23	%
density		ASTM D792/ISO 1183	1.2
Shrinkage rate		ASTM D955	0.5-0.7	%
melt mass-flow rate		ASTM D1238/ISO 1133	40 cm3/10min(300℃/1.2kg )	g/10min
Water absorption rate		ASTM D570/ISO 62	0.23	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.