PPO(PPE)+PS+PP

PPO(PPE)+PS+PP NORYL PPX™ PPX830 resin SABIC

Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	42 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	42 kJ/m²
Dart impact	-30°C,TotalEnergy	ASTM D3763	10.0 J
Impact strength of cantilever beam gap	23°C	ASTM D4812	650 J/m
	Impact strength of cantilever beam gap	23°C	ISO 180/1A	10 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D256	95 J/m
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	39 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	36 kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	15.0 J

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.0mm	UL 94	HB
Burning wire flammability index	3.0mm	IEC 60695-2-12	650 °C

mechanical properties	Test Condition	Test Method	Test Result
bending strength	Yield,50.0mmSpan	ASTM D790	144 MPa
tensile strength	Yield	ASTM D638	101 MPa
Tensile modulus		ISO 527-2/1	7700 MPa
bending strength		ISO 178	141 MPa
Bending modulus		ISO 178	7100 MPa
Bending modulus	Bending modulus	50.0mmSpan	ASTM D790	6600 MPa
Tensile strain	Break	ISO 527-2/5	3.2 %
elongation	Break	ASTM D638	100 %
Tensile strain	Yield	ISO 527-2/5	3.2 %
elongation	Yield	ASTM D638	2.9 %
tensile strength	Break	ISO 527-2/5	98.0 MPa
	tensile strength	Break	ASTM D638	101 MPa
	tensile strength	tensile strength	Yield	ISO 527-2/5	98.0 MPa
Tensile modulus		ASTM D638	7600 MPa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	TD：-30to80°C	ISO 11359-2	1.2E-04 cm/cm/°C
	Linear coefficient of thermal expansion	TD：-40to95°C	ASTME831	1.3E-04 cm/cm/°C
		Linear coefficient of thermal expansion	MD：-30to80°C	ISO 11359-2	2.5E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：-40to95°C	ASTME831	2.5E-05 cm/cm/°C
Ball Pressure Test	125°C	IEC 60695-10-2	Pass
Vicat softening temperature		ISO 306/B120	150 °C
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	166 °C
	Hot deformation temperature	0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	168 °C
		Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	156 °C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	153 °C

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792	1.19 g/cm³
density	density		ISO 1183	1.19 g/cm³
melt mass-flow rate	280°C/5.0kg	ASTM D1238	6.0 g/10min
Melt Volume Flow Rate (MVR)	280°C/5.0kg	ISO 1133	6.00 cm³/10min
Shrinkage rate	MD：3.20mm	Internal Method	0.20to0.25 %
Shrinkage rate	Shrinkage rate	TD：3.20mm	Internal Method	0.40to0.60 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.