Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Thermosetting components | | | 按重量计算的混合比:0.50 |
| Thermosetting components | | | 100 |
| Thermosetting components | Shelf Life | | 26 wk |
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| Color | | | White |
| Viscosity | | | 14to18 Pa·s |
| Curing Time | | | 12to16 hr |
| Curing Time | | | 16to24 hr |
| STORAGE STABILITY | | | 60to120 min |
| STORAGE STABILITY | | | 120to240 min |
| Cured Properties | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | | 5E-03 |
| Shore hardness | | | 150to200 % |
| Shore hardness | | | 1.75to5.25 kN/m |
| Shore hardness | | | 20 kV/mm |
| Shore hardness | | | 3.60 |
| Shore hardness | | | 2E+14 ohms·cm |
| Shore hardness | | | 40 |
| Shore hardness | | | 42 |
| Shore hardness | | | 2.41to2.76 MPa |
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | | 1.21 g/cm³ |
| Shrinkage rate | | | 0.10 % |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|
| ThermalConductivityofMelt-Cured | | | 0.26 W/m/K |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| SpecificHeatCapacity-Cured | | | 1460 J/kg/°C |
| Linear coefficient of thermal expansion | | | 2.2E-04 cm/cm/°C |
| Usage temperature | | | -115-204 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.