PP T30S Hunan Changsheng

Form：Granules | Grade：Withdrawal level

Properties:

high strength

Typical Applications:

building materialsCarpet backingCharger casing

Supplier(0)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	building materials \| Carpet backing \| Charger casing
Properties:	high strength

Certificates

No Data...

Technical Data Sheet

Other performance	Test Condition	Test Method	Test Result	Test Unit
Huangdu Index		QJ/CL.4.3.13	合格｜≤4	%
	Huangdu Index		QJ/CL.4.3.13	一等｜≤4	%
	Huangdu Index	Huangdu Index		QJ/CL.4.3.13	优等｜≤4	%
Isotropy		QJ/CL.4.3.10	合格｜≥94.0	%
ash content		QJ/CL.4.3.11	一等｜≤300	ppm
ash content	ash content		QJ/CL.4.3.11	优等｜≤200	ppm
Chlorine content		QJ/CL.4.3.12	合格｜≤50	ppm
	Chlorine content		QJ/CL.4.3.12	一等｜≤50	ppm
	Chlorine content	Chlorine content		QJ/CL.4.3.12	优等｜≤50	ppm
Isotropy		QJ/CL.4.3.10	一等｜≥96.0	%
Isotropy	Isotropy		QJ/CL.4.3.10	优等｜≥96.0	%
ash content		QJ/CL.4.3.11	合格｜≤300	ppm
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate		QJ/CL.4.3.9	合格｜2.0-3.9	g/10min
	melt mass-flow rate		QJ/CL.4.3.9	一等｜2.3-3.7	g/10min
	melt mass-flow rate	melt mass-flow rate		QJ/CL.4.3.9	优等｜2.5-3.5	g/10min
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Bending modulus		QJ/CL.4.3.18	一等｜≥1300	Mpa
	Bending modulus		QJ/CL.4.3.18	合格｜≥1280	Mpa
	Bending modulus	Bending modulus		QJ/CL.4.3.18	优等｜≥1320	Mpa
Rockwell hardness		QJ/CL.4.3.16	合格｜≥90	R
Impact strength of cantilever beam gap	23℃	QJ/CL.4.3.19	一等｜≥35	J/m
Rockwell hardness		QJ/CL.4.3.16	一等｜≥90	R
Rockwell hardness	Rockwell hardness		QJ/CL.4.3.16	优等｜≥90	R
Impact strength of cantilever beam gap	23℃	QJ/CL.4.3.19	合格｜≥35	J/m
tensile strength	Yield	QJ/CL.4.3.17	优等｜≥33	Mpa
	tensile strength	Yield	QJ/CL.4.3.17	一等｜≥31	Mpa
	tensile strength	tensile strength	Yield	QJ/CL.4.3.17	合格｜≥29	Mpa
Impact strength of cantilever beam gap	23℃	QJ/CL.4.3.19	优等｜≥35	J/m
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature		QJ/CL.4.3.15	优等｜≥153	°C
Hot deformation temperature	HDT	QJ/CL.4.3.14	合格｜≥86	°C
	Hot deformation temperature	HDT	QJ/CL.4.3.14	一等｜≥96.0	°C
	Hot deformation temperature	Hot deformation temperature	HDT	QJ/CL.4.3.14	优等｜≥96.0	°C
Vicat softening temperature		QJ/CL.4.3.15	合格｜≥150	°C
Vicat softening temperature	Vicat softening temperature		QJ/CL.4.3.15	一等｜≥153	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.