Technical Data Sheet
| thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO 75-2/Af | 240 °C |
| vicat | -- | ISO 306/A50 | >250 °C |
| vicat | -- | ISO 306/B50 | 215 °C |
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/Bf | >250 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | 0.75mm | IEC 60695-2-13 | 875 °C |
| Hot filament ignition temperature | 1.5mm | IEC 60695-2-13 | 875 °C |
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 875 °C |
| UL flame retardant rating | 0.8mm | IEC 60695-11-10,-20 | V-0 |
| UL flame retardant rating | 1.6mm | IEC 60695-11-10,-20 | V-0 |
| UL flame retardant rating | 3.2mm | IEC 60695-11-10,-20 | V-0 |
| Burning wire flammability index | 0.75mm | IEC 60695-2-12 | 960 °C |
| Burning wire flammability index | 1.5mm | IEC 60695-2-12 | 960 °C |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183/A | 1.72 g/cm³ |
| Melt volume flow rate | 300°C/2.16kg | ISO 1133 | 25.0 cm³/10min |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 2 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile modulus | | ISO 527-2/1A/1 | 11900 MPa |
| tensile strength | Break | ISO 527-2/1A/5 | 100 MPa |
| Tensile strain | Break | ISO 527-2/1A/5 | 1.2 % |
| flexural modulus | | ISO 178 | 7750 MPa |
| bending strength | 1.6%Strain | ISO 178 | 142 MPa |
| impact performance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 5.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 20 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.