Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | g/cm³ | 1.33 -- |
| Shrinkage rate | | % | 0.40 0.80 |
| Water absorption rate | | % | 7.0 -- |
| Water absorption rate | | % | 2.5 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | | 115 100 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Hot filament ignition temperature | | °C | 650 -- |
| UL flame retardant rating | | | HB -- |
| UL flame retardant rating | | | HB -- |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Break | MPa | 155 90.0 |
| elongation | Break | % | 3.5 7.0 |
| Flexural modulus | | MPa | 7000 4000 |
| bending strength | Break | MPa | 210 130 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | J/m | 60 100 |
| Impact strength of cantilever beam gap | | J/m | 90 120 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| | | 3.80 4.20 |
| Dissipation Factor | | | 0.020 0.12 |
| Surface Resistivity | | ohms | 1E+14 1E+13 |
| Volume resistivity | | ohms·cm | 1E+15 1E+12 |
| dielectric strength | | kV/mm | 34 24 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | °C | 200 -- |
| Crystallization peak temperature | | °C | 220 -- |
| | cm/cm/°C | 4E-05 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.