Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.45 g/cm³ |
| SpiralFlow | | 内部方法 | 48.0 cm |
| Shrinkage rate | | ISO294-4 | 0.80 % |
| Shrinkage rate | | ISO294-4 | 0.30 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | FMVSS302 | <100 mm/min |
| FlameRating | | UL94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ReinforcementContent | | ISO1172 | 40 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 14 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 14 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 18 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 110 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 110 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 110 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | 14 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | 20 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2/1 | 12800 MPa |
| Tensile stress | Break | ISO527-2/5 | 210 MPa |
| Tensile strain | Break | ISO527-2/5 | 4.0 % |
| Flexural modulus | | ISO178 | 10300 MPa |
| Bending stress | | ISO178 | 300 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/A | 215 °C |
| melting temperature | | DINEN11357-1 | 222 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare