Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.48 g/cm³ |
| melt mass-flow rate | | ISO1133 | 39 g/10min |
| Melt volume flow rate | | ISO1133 | 31.0 cm3/10min |
| Water absorption rate | | ISO62 | 0.50 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO2039-2 | 90 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ColorNumber | | | CF2001 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 3700 Mpa |
| Tensile stress | | ISO527-2 | 57.0 Mpa |
| Tensile strain | | ISO527-2 | 5.0 % |
| Flexural modulus | | ISO178 | 3500 Mpa |
| Bending stress | | ISO178 | 90.0 Mpa |
| | JISK7218 | 0.34 |
| | JISK7218 | 0.44 |
| Wear factor | | JISK7218 | 10 10^-8mm³/N·m |
| Wear factor | | JISK7218 | 600 10^-8mm³/N·m |
| Wear factor | | JISK7218 | 2500 10^-8mm³/N·m |
| Wear factor | | JISK7218 | 5000 10^-8mm³/N·m |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 3.3 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 2E+16 ohms |
| Volume resistivity | | IEC60093 | 3E+14 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/A | 112 °C |
| | 内部方法 | 9E-05 cm/cm/°C |
| | 内部方法 | 9E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.