GPPS PG-383 TAIWAN CHIMEI

Form：Granules | Grade：Injection grade

Properties:

high strengthheat-resisting

Typical Applications:

Food service sector

Supplier(1)

Product Description

Certificates(3)

Datasheet

Alternative Model(1)

Product Description

Typical Applications:	Food service sector
Properties:	high strength \| heat-resisting

Certificates

MSDS

RoHS

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-30°C	ISO 179	2.5	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179	3.0	kJ/m²
Impact strength of cantilever beam gap	23°C,3.20mm	ASTM D256	18	J/m
	Impact strength of cantilever beam gap	23°C,6.40mm	ASTM D256	17	J/m
		Impact strength of cantilever beam gap	-30°C	ISO 180/1A	1.8	kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	2.0	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ISO 178	82.0	Mpa
tensile strength	Break	ASTM D638	53.8	Mpa
tensile strength	tensile strength	Break	ISO 527-2/50	54.0	Mpa
elongation	Break	ASTM D638	2.0	%
Tensile strain	Break	ISO 527-2/50	6.0	%
Bending modulus		ASTM D790	3240	Mpa
Bending modulus	Bending modulus		ISO 178	2500	Mpa
bending strength		ASTM D790	80.3	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	89.0	°C
	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	85.0	°C
		Hot deformation temperature	1.8MPa,Annealed	ASTM D648	99.0	°C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	99.0	°C
Vicat softening temperature		ASTM D15256	105	°C
	Vicat softening temperature	--	ISO 306/A50	106	°C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	103	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	5.0E-5to8.0E-5	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density	比重	ASTM D792	1.05	g/cm³
density	density	23°C	ISO 1183	1.05	g/cm³
melt mass-flow rate	200°C/5.0kg	ASTM D1238	2.2	g/10min
Melt Volume Flow Rate (MVR)	200°C/5.0kg	ISO 1133	2.50	cm3/10min
Shrinkage rate		ISO 294-4	0.40-0.70	%
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M-Scale	ASTM D785	82

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.