Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.15 g/cm³ |
| Melt volume flow rate | | ISO 1133 | 10.0 cm³/10min |
| Shrinkage rate | | ISO 294-4 | 1.1to1.4 % |
| Water absorption rate | | ISO 62 | 1.3 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179 | 160 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/A | 8.0 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/A | 10 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 2900 MPa |
| tensile strength | | ISO 527-2 | 50.0 MPa |
| Tensile strain | | ISO 527-2 | 3.0 % |
| Tensile strain | | ISO 527-2 | >10 % |
| Flexural modulus | | ISO 178 | 3000 MPa |
| bending strength | | ISO 178 | 88.0 MPa |
| film | Test Condition | Test Method | Test Result |
|---|
| elongation | Break | ISO 527-3 | >10 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC 60093 | 1E+15 ohms·cm |
| Dissipation Factor | | IEC 60250 | 7.5E-03 |
| Dissipation Factor | | IEC 60250 | 0.015 |
| Surface Resistivity | | IEC 60093 | 1E+15 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 132 °C |
| Heat distortion temperature | | ISO 75-2/A | 92.0 °C |
| vicat | | ASTM D15253 | 245 °C |
| vicat | | ISO 306/B50 | 160 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 8E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.