Technical Data Sheet
| 物理性能 | Test Condition | Test Method | Test Result |
|---|
| 熔体质量流动速率 | 220°C/10.0 kg | ASTM D1238 | 21 g/10 min |
| 收缩率 - 流动 | 23°C, 3.20 mm, 注塑 | ASTM D955 | 0.40 到 0.70 % |
| 熔体质量流动速率(MFR)220℃/10 kg | / | ASTM D 1238 | 20.621 g/10 min |
| 热性能 | Test Condition | Test Method | Test Result |
|---|
| 载荷下热变形温度 | 1.8 MPa, 未退火, 6.40 mm, 注塑 | ASTM D648 | 81.0 °C |
| 维卡软化温度 | | ASTM D15257 | 89.0 °C |
| RTI Elec | | UL 746 | 50.0 °C |
| RTI Imp | | UL 746 | 50.0 °C |
| RTI | | UL 746 | 50.0 °C |
| 光学性能 | Test Condition | Test Method | Test Result |
|---|
| 透射率 | 3200 µm, 注塑 | ASTM D1003 | 90.0 % |
| 雾度 | 注塑 | ASTM D1003 | 2.0 % |
| 透光率 |
Rate B/50 | ASTM D1003 | 90 % |
| 雾度 | -40°C to | ASTM D1003 | 2 % |
| 可燃性 | Test Condition | Test Method | Test Result |
|---|
| UL阻燃等级 | 1.5 mm | UL 94 | HB |
| UL阻燃等级 | 3.0 mm | UL 94 | HB |
| 机械性能 | Test Condition | Test Method | Test Result |
|---|
| 拉伸模量 | 23°C, 3.20 mm, 注塑 | ASTM D638 | 2050 Mpa |
| 抗张强度 | 屈服, 23°C, 3.20 mm, 注塑 | ASTM D638 | 48.0 Mpa |
| 伸长率 4 | 屈服, 23°C, 3.20 mm, 注塑 | ASTM D638 | > 5.0 % |
| 伸长率 4 | 断裂, 23°C, 3.20 mm, 注塑 | ASTM D638 | 15 % |
| 弯曲模量 | 23°C, 3.20 mm, 注塑 | ASTM D790 | 2250 Mpa |
| 弯曲强度 | 23°C, 3.20 mm, 注塑 | ASTM D790 | 71.0 Mpa |
| 拉伸强度屈服(yld) | 3.2mm, 5 | ASTM D638 | 470 kg/cm2 |
| 拉伸延伸率断裂(brk) | 3.2mm, 5 | ASTM D638 | 30 % |
| 弯曲强度 | 3.2mm, 1 | ASTM D790 | 700 kg/cm2 |
| 弯曲模量 | 3.2mm, 1 | ASTM D790 | 22000 kg/cm2 |
| 注射 | Test Condition | Test Method | Test Result |
|---|
| 干燥温度 | | | 80 到 90 °C |
| 干燥时间 | | | 2.0 到 4.0 hr |
| 料筒后部温度 | | | 180 到 200 °C |
| 料筒中部温度 | | | 190 到 210 °C |
| 料筒前部温度 | | | 200 到 220 °C |
| 射嘴温度 | | | 190 到 220 °C |
| 加工（熔体）温度 | | | 190 到 220 °C |
| 模具温度 | | | 40 到 60 °C |
| 背压 | | | 29.4 到 58.8 Mpa |
| 螺杆转速 | | | 30 到 60 rpm |
| 硬度 | Test Condition | Test Method | Test Result |
|---|
| 洛氏硬度 | R 级, 23°C, 注塑 | ASTM D785 | 107 |
| 洛氏硬度R | | ASTM D785 | 107 R |
| 冲击性能 | Test Condition | Test Method | Test Result |
|---|
| 悬臂梁缺口(Izod Notched)23℃ (73℉) | 3.2mm | ASTM D256 | 17 kg·cm/cm |
| 悬臂梁缺口(Izod Notched)23℃ (73℉) | 6.4mm | ASTM D256 | 17 kg·cm/cm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare