Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO 1133 | 0.9 g/10min |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|
| vicat | | ISO 306/A50 | 145 °C |
| melting temperature | | ISO 11357-3 | 163 °C |
| RTI Imp | | UL 746B | 75 °C |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ISO 868 | 57 D |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| gloss | | ASTM D 2457 | 57 - mm |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ISO 527-1/-2 | 20 Mpa |
| tensile strength | | ISO 527-1/-2 | 30 Mpa |
| elongation | | ISO 527-1/-2 | 12 % |
| elongation at break | | ISO 527-1/-2 | 500 % |
| tear strength | | ASTM D 624 | 67 kN/m |
| Flexural modulus | | ISO 178 | 800 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO 179 | 5 kJ/m² |
| Suspended wall beam without notch impact strength | | ISO 179 | 10 kJ/m² |
| Suspended wall beam without notch impact strength | | ISO 179 | 95 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.