Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | | <0.10 % |
| Water absorption rate | | GB/T1034 | 0.20到0.30 % |
| PVLimit | | | 1600 |
| density | | GB/T1033 | 1.65 g/cm³ |
| melt mass-flow rate | | GB/T3682 | 15到30 g/10min |
| Shrinkage rate | | | <0.20 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | GB/T9342 | 65 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | Break | GB/T1040 | 0.30 % |
| Bending stress | | GB/T1042 | 150 MPa |
| compression stress | | GB/T1041 | 235 MPa |
| | GB/T3960 | 0.020 |
| Abrasion | | | 1 µm |
| Tensile stress | | GB/T1040 | 80.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | GB/T1043 | 5.0 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | GB/T2572 | -2E-05 cm/cm/°C |
| | GB/T2572 | -3.5E-05 cm/cm/°C |
| Heat distortion temperature | | GB/T1634 | >265 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.