Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
density | | ASTM D792 | 1.29 g/cm³ |
melt mass-flow rate | | ASTM D1238 | 25 g/10min |
Shrinkage rate | | ASTM D955 | 0.70to0.90 % |
Shrinkage rate | | ASTM D955 | 1.0to1.2 % |
Water absorption rate | | ASTM D570 | 0.20 % |
hardness | Test Condition | Test Method | Test Result |
---|
Rockwell hardness | M-Scale | ASTM D785 | 94 |
flammability | Test Condition | Test Method | Test Result |
---|
UL flame retardant rating | | UL 94 | V-0 |
UL flame retardant rating | | UL 94 | V-0 |
Filling analysis | Test Condition | Test Method | Test Result |
---|
melt viscosity | | ASTM D3835 | 240 Pa·s |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
tensile strength | | ASTM D638 | 87.0 MPa |
elongation | | ASTM D638 | 6.2 % |
elongation | Yield | ISO 527-2/1A/50 | 5.7 % |
elongation | | ASTM D638 | >40 % |
elongation | Break | ISO 527-2/1A/50 | >40 % |
Flexural modulus | | ASTM D790 | 3100 MPa |
Flexural modulus | | ISO 178 | 3200 MPa |
Tensile modulus | | ISO 527-2/1A/1 | 3200 MPa |
tensile strength | Yield | ISO 527-2/1A/50 | 89.0 MPa |
shear strength | | ASTM D732 | 78.0 MPa |
bending strength | | ASTM D790 | 124 MPa |
bending strength | | ISO 178 | 127 MPa |
compressive strength | | ASTM D695 | 112 MPa |
Tensile modulus | | ASTM D638 | 3000 MPa |
Impact resistance | Test Condition | Test Method | Test Result |
---|
Impact strength of cantilever beam gap | | ASTM D256 | 69 J/m |
Impact strength of cantilever beam gap | | ISO 180 | 6.6 kJ/m² |
Suspended wall beam without notch impact strength | | ASTMD256 | 无断裂 |
Electrical performance | Test Condition | Test Method | Test Result |
---|
Surface Resistivity | | ASTM D257 | >1.9E+17 ohms |
Volume resistivity | | ASTM D257 | 5E+17 ohms·cm |
dielectric strength | | ASTM D149 | 16 kV/mm |
dielectric constant | | ASTM D150 | 3.10 |
dielectric constant | | ASTM D150 | 3.12 |
dielectric constant | | ASTM D150 | 3.10 |
Dissipation Factor | | ASTM D150 | 1E-03 |
Dissipation Factor | | ASTM D150 | 1E-03 |
Dissipation Factor | | ASTM D150 | 4E-03 |
Thermal performance | Test Condition | Test Method | Test Result |
---|
thermal conductivity | | ASTME1530 | 0.24 W/m/K |
Heat distortion temperature | | ASTM D648 | 190 °C |
Glass Transition Temperature | | ASTM D3418 | 158 °C |
melting temperature | | ASTM D3418 | 345 °C |
Linear coefficient of thermal expansion | | ASTME831 | 4.7E-05 cm/cm/°C |
specific heat | | DSC | 1310 J/kg/°C |
specific heat | | DSC | 1820 J/kg/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.