PC Tuffak® CM-2 France Arkema Altuglas

Compare

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
turbidity	6.35μm	ASTM D1003	0.50to2.0 %
transmissivity	6350μm	ASTM D1003	85.0to91.0 %
Refractive index		ASTM D542	1.586

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	3.18mm	ASTM D256	850 J/m
Charpy Notched Impact Strength	6.35mm	ASTM D256	无断裂

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	6.35mm	ASTM D638	2340 MPa
Bending modulus	6.35mm	ASTM D790	2340 MPa
elongation	Yield,6.35mm	ASTM D638	100 %
tensile strength	Ultimate,6.35mm	ASTM D638	65.5 MPa
shear strength	6.35mm	ASTM D732	40.0 MPa
compressive strength	6.35mm	ASTM D695	86.2 MPa
bending strength	Yield,6.35mm	ASTM D790	93.1 MPa
tensile strength	Yield,6.35mm	ASTM D638	57.9 MPa

thermal performance	Test Condition	Test Method	Test Result
thermal conductivity		ASTMC177	0.19 W/m/K
specific heat		ASTMC351	1260 J/kg/°C
Linear coefficient of thermal expansion	MD：6.35mm	ASTM D696	6.8E-05 cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed,6.35mm	ASTM D648	135 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,6.35mm	ASTM D648	141 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium,100°C	ASTM D570	0.58 %
	Water absorption rate	Equilibrium,23°C	ASTM D570	0.35 %
	Water absorption rate	Water absorption rate	23°C,24hr	ASTM D570	0.15 %
density		ASTM D792	1.20 g/cm³

Electrical performance	Test Condition	Test Method	Test Result
Dielectric constant	6.35mm,1MHz	ASTM D150	2.90
Dielectric constant	Dielectric constant	6.35mm,60Hz	ASTM D150	2.90
Dielectric strength	3.18mm	ASTM D149	15 kV/mm
Volume resistivity		ASTM D257	1E+16 ohms·cm

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	M-Scale,6.35mm	ASTM D785	74
Rockwell hardness	Rockwell hardness	R-Scale,6.35mm	ASTM D785	118

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.