PEI KMI PEI KM-H00R IEP
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 1.30 g/cm³ | |
| Shrinkage rate | ASTM D995 | 0.50-0.70 % | |
| Water absorption rate | ASTM D570 | 0.25 % | |
| melt mass-flow rate | ASTM D1238 | 9.0 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ASTM D638 | 125 MPa | |
| elongation at break | ASTM D638 | 13 % | |
| bending strength | ASTM D790 | 160 MPa | |
| Flexural modulus | ASTM D790 | 3500 MPa | |
| Impact strength of cantilever beam gap | ASTM D256 | 65 J/m |
| Flame retardant performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL -94 | V-0 . |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | ASTM D257 | >1.0E+15 Ω.cm | |
| dielectric strength | ASTM D149 | 28 KV/mm | |
| dielectric constant | ASTM D150 | 3.10 | |
| Dissipation Factor | ASTM D150 | 0.015 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 208 °C | |
| vicat | Melting Temperature | ASTM D3418 | 340 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.