Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.27 g/cm³ |
| Shrinkage rate | | | 0.40to0.80 % |
| Water absorption rate | | | 2.6 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTMD785 | 102 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| FlameRating | | UL94 | HB |
| Burning wire flammability index | | IEC60695-2-12 | 650 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179 | 8.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179 | 30 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180 | 60 J/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | Break | ISO527-2 | 3.5 % |
| Flexural modulus | | ISO178 | 5500 MPa |
| Tensile modulus | | ISO527-2 | 6500 MPa |
| Tensile stress | Break | ISO527-2 | 115 MPa |
| Bending stress | | ISO178 | 200 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | DIN53482 | 1E+12 ohms |
| Volume resistivity | | DIN53482 | 1E+15 ohms·cm |
| CTI | | IEC60112 | 600 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 200 °C |
| | ISO75-2/A | 190 °C |
| | ISO3146 | 220 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.